Abstract: Free-radical copolymerization of 2-hydroxyethyl methacrylate with 2-hydroxyethyl acrylate can be successively utilized for the synthesis of water-soluble polymers and hydrogels with excellent physicochemical properties, thus showing promise for pharmaceutical and biomedical applications. In the work presented it has been demonstrated that water-soluble copolymers based on 2-hydroxyethyl methacrylate and 2-hydroxyethyl acrylate exhibit lower critical solution temperature in aqueous solutions, whereas the corresponding high molecular weight homopolymers do not have this unique property. The temperature-induced transitions observed upon heating the aqueous solutions of these copolymers proceed via liquid-liquid phase separation. The hydrogels were also synthesized by copolymerizing 2-hydroxyethyl methacrylate and 2-hydroxyethyl acrylate in the absence of a bifunctional cross-linker. The cross-linking of these copolymers during copolymerization is believed to be due to the presence of bifunctional admixtures or transesterification reactions. Transparency, swelling behavior, mechanical properties, and porosity of the hydrogels are dependent upon the monomer ratio in the copolymers. Hydrogel samples containing more 2-hydroxyethyl methacrylate are less transparent, have lower swelling capacity, higher elastic moduli, and pores of smaller size. The assessment of the biocompatibility of the copolymers using the slug mucosal irritation test revealed that they are also less irritant than poly(acrylic acid).

Abstract: Mucoadhesive polymeric films have been prepared based on blends of chitosan and hydroxyethylcellulose. The blends have been characterized by IR spectroscopy, DSC, WAXD, TGA, SEM, and mechanical testing. It is demonstrated that the mechanical properties of chitosan are improved significantly upon blending with hydroxyethylcellulose. An increase in hydroxyethylcellulose content in the blends makes the materials more elastic. The thermal treatment of the blends at 100 degrees C leads to partial cross-linking of the polymers and formation of water-insoluble but swellable materials. The adhesion of the films towards porcine buccal mucosa decreases with increasing hydroxyethylcellulose content in the blends.

Abstract: Chitosan is a biocompatible and biodegradable amino polysaccharide, which is soluble in aqueous solutions at pH < 6.5. It has been widely used for developing drug delivery systems because of its excellent mucoadhesive properties. Although many studies report on chitosan being mucoadhesive, the nature of interactions between chitosan and mucin remains poorly defined. Here, we have examined the role of primary amino groups and the role of electrostatic attraction, hydrogen bonding, and hydrophobic effects on aggregation of gastric mucin in the presence of chitosan. Reducing the number of amino groups through their half acetylation results in expansion of chitosan's pH-solubility window up to pH 7.4 but also reduces its capacity to aggregate mucin. We demonstrated that electrostatic attraction forces between chitosan and gastric mucin can be suppressed in the presence of 0.2 mol/L sodium chloride; however, this does not prevent the aggregation of mucin particles in the presence of this biopolymer. The presence of 8 mol/L urea or 10% v/v ethanol in solutions also affects mucin aggregation in the presence of chitosan, demonstrating the role of hydrogen bonding and hydrophobic effects, respectively, in mucoadhesion.

Abstract: The formation of hydrogen-bonded interpolymer complexes between poly(acrylic acid) and poly( N-vinyl pyrrolidone) as well as amphiphilic copolymers of N-vinyl pyrrolidone with vinyl propyl ether has been studied in aqueous and organic solutions. It was demonstrated that introduction of vinyl propyl ether units into the macromolecules of the nonionic polymer enhances their ability to form complexes in aqueous solutions due to more significant contribution of hydrophobic effects. The complexation was found to be a multistage process that involves the formation of primary polycomplex particles, which further aggregate to form spherical nanoparticles. Depending on the environmental factors (pH, solvent nature), these nanoparticles may either form stable colloidal solutions or undergo further aggregation, resulting in precipitation of interpolymer complexes. In organic solvents, the intensity of complex formation increases in the following order: methanol < ethanol < isopropanol < dioxane. The multilayered coatings were developed using layer-by-layer deposition of interpolymer complexes on glass surfaces. It was demonstrated that the solvent nature affects the efficiency of coating deposition.

Abstract: Association of poly(carboxylic acids) and non-ionic polymers in solutions via hydrogen bonding results in formation of novel polymeric materials--interpolymer complexes. These materials can potentially be used for design of novel mucoadhesive dosage forms, development of solid drug dispersions and solubilisation of poorly soluble drugs, encapsulation technologies, preparation of nanoparticles, hydrogels, in situ gelling systems and electrically erodible materials. This review is an attempt to analyse and systematise existing literature on pharmaceutical application of hydrogen-bonded interpolymer complexes.

Abstract: Three series of water-soluble cationic copolymers have been synthesised by free-radical copolymerisation of [2-(methacryloyloxy)ethyl]trimethylammonium chloride (MADQUAT) with methyl acrylate (MA), butyl acrylate (BA) and butyl methacrylate (BMA). The interactions between these copolymers and porcine stomach mucin have been studied in aqueous solutions using dynamic light scattering, zeta-potential measurements, turbidimetric titration and transmission electron microscopy (TEM). It was demonstrated that mixing aqueous dispersions of mucin with solutions of the cationic copolymers results in significant changes in size distribution and zeta-potential of its particles. It was found that an increase in the content of hydrophobic groups in copolymers leads to more efficient adsorption of macromolecules on the surface of mucin particles, which evidences the importance of hydrophobic effects in mucoadhesion. The efficiency of mucoadhesive interactions was found to be significantly dependent on pH, which affects the surface charge and aggregation stability of mucin.

Abstract: Amphiphilic chitosan-based polymers (Mw < 20 kDa) self-assemble in aqueous media at low micromolar concentrations to give previously unknown micellar clusters of 100-300 nm in size. Micellar clusters comprise smaller 10-30 nm aggregates, and the nanopolarity/drug incorporation efficiency of their hydrophobic domains can be tailored by varying the degree of lipidic derivatization and molecular weight of the carbohydrate. The extent of drug incorporation by these novel micellar clusters is 1 order of magnitude higher than is seen with triblock copolymers, with molar polymer/drug ratios of 1:48 to 1:67. On intravenous injection, the pharmacodynamic activity of a carbohydrate propofol formulation is increased by 1 order of magnitude when compared to a commercial emulsion formulation, and on topical ocular application of a carbohydrate prednisolone formulation, initial drug aqueous humor levels are similar to those found with a 10-fold dose of prednisolone suspension.

Abstract: Mixing of aqueous solutions of poly(acrylic acid) and (hydroxypropyl)cellulose results in formation of hydrogen-bonded interpolymer complexes, which precipitate and do not allow preparation of homogeneous polymeric films by casting. In the present work the effect of pH on the complexation between poly(acrylic acid) and (hydroxypropyl)cellulose in solutions and miscibility of these polymers in solid state has been studied. The pH-induced complexation-miscibility-immiscibility transitions in the polymer mixtures have been observed. The optimal conditions for preparation of homogeneous polymeric films based on blends of these polymers have been found, and the possibility of radiation cross-linking of these materials has been demonstrated. Although the gamma-radiation treatment of solid polymeric blends was found to be inefficient, successful cross-linking was achieved by addition of N,N'-methylenebis(acrylamide). The mucoadhesive potential of both soluble and cross-linked films toward porcine buccal mucosa is evaluated. Soluble films adhered to mucosal tissues undergo dissolution within 30-110 min depending on the polymer ratio in the blend. Cross-linked films are retained on the mucosal surface for 10-40 min and then detach.

Abstract: The effect of pH on the complexation of poly(acrylic acid) with poly(vinyl alcohol) in aqueous solution, the miscibility of these polymers in the solid state and the possibility for crosslinking the blends using gamma radiation has been studied. It is demonstrated that the complexation ability of poly(vinyl alcohol) with respect to poly(acrylic acid) is relatively low in comparison with some other synthetic non-ionic polymers. The precipitation of interpolymer complexes was observed below the critical pH of complexation (pH(crit1)), which characterizes the transition between a compact hydrophobic polycomplex and an extended hydrophilic interpolymer associate. Films prepared by casting from aqueous solutions at different pH values exhibited a transition from miscibility to immiscibility at a certain critical pH, pH(crit2), above which hydrogen bonding is prevented. It is shown here that gamma radiation crosslinking of solid blends is efficient and only results in the formation of hydrogel films for blends prepared between pH(crit1) and pH(crit2). The yield of the gel fraction and the swelling properties of the films depended on the absorbed radiation dose and the polymer ratio. [Diagram: see text] SEM image of an equimolar PAA-PVA blend cast from a pH 4.6 solution.

Abstract: The effect of pH on the complex formation between poly(acrylic acid) (PAA) and poly(ethylene oxide) (PEO) has been studied in aqueous solutions by turbidimetric and fluorescent methods. It was shown that the formation of insoluble interpolymer complexes is observed below a certain critical pH of complexation (pH(crit1)). The formation of hydrophilic interpolymer associates is possible above pH(crit1) and below a certain pH(crit2). The effects of polymer concentrations in solution and PEO molecular weight as well as inorganic salt addition on these critical pH values were studied. The polymeric films based on blends of PAA and PEO were prepared by casting from aqueous solutions with different pHs. These films were characterized by light transmittance measurements and differential scanning calorimetry. The existence of the pH value above which the polymers form an immiscible blend was demonstrated. The transitions between the interpolymer complex, miscible blend, and immiscible blend caused by pH changes are discussed. The recommendations for preparation of homogeneous miscible films based on compositions of poly(carboxylic acids) and various nonionic water-soluble polymers are presented.